X6S Dielectric, KGM Series
Specications and Test Methods
TDS-SMDMLCC-0044 | Rev 3
X6S Specication Limits X6S Specication Limits Measuring Conditions (Complies with JIS C5101 / IEC60384)
Operating Temperature Range -55ºC to +105ºC Temperature Cycle Chamber
Capacitance Within specied tolerance Measure after heat treatment
Capacitance Frequency Volt
C≤10µF
Frequency : 1kHz±10%
Volt : 1.0±0.2Vrms *0.5±0.2Vrms
C>10µF
Frequency : 120Hz±10%
Volt : 0.5±0.2Vrms
The charge and discharge current of the capacitor must
not exceed 50mA.
Dissipation Factor / Tanδ
Refer to https://spicat.kyocera-avx.com for individual part
number specication
Insulation Resistance
Refer to https://spicat.kyocera-avx.com for individual part
number speciction
Apply the rated voltage for 1 minute, and measure it in normal temperature and humidity.
The charge and discharge current of the capacitor must not exceed 50mA.
Dielectric Strength No breakdown or visual defects
Charge device with 250% of rated voltage for 1-5 seconds, w/charge and discharge current limited to 50 mA (max)
* Note, Charge device with 150% rated voltage for 500V devices
Bending Strength No signicant damage with 1mm bending Glass epoxy PCB: Fulcrum spacing: 90mm, duration time 10 seconds.
Solderability Solder coverage : 95% min. Soaking condition Sn-3Ag-0.5Cu 245±5℃ 3±0.5 sec.
Resistance to
Solder Heat
Appearance No problem observed
Take the initial value after heat treatment.
Soak the sample in 260℃±5℃ solder for 10±0.5 seconds and place in normal temperature and humidity, and measure
after heat treatment.
(Pre-heating conditions)
Order Temperature Time
1 80 to 100℃ 2 minutes
2 150 to 200℃ 2 minutes
The charge and discharge current of the capacitor must not exceed 50mA for IR and withstanding voltage measurement.
Capacitance Variation ≤ ±7.5%
Dissipation Factor/ Tanδ Within specication
Insulation Resistance Within specication
Withstanding Voltage / Dielectric
Strength
Resist without problem
Thermal Shock
Appearance No visual defects
Take the initial value after heat treatment.
(Cycle)
Room temperature (3 min.)→
Lowest operation temperature (30 min.)→
Room temperature (3 min.)→
Highest operation temperature (30 min.)
After 5 cycles, measure after heat treatment.
The charge and discharge current of the capacitor must not exceed 50mA for IR and withstanding voltage measurement.
Capacitance Variation ≤ ±7.5%
Dissipation Factor Within specication
Insulation Resistance Within specication
Withstanding Voltage / Dielectric
Strength
Resist without problem
Load Life
Appearance No visual defects
Take the initial value after heat treatment.
After applying *1.5 the rated voltage at the highest operation temperature for 1000+12/ −0 hours, and measure the
sample after heat treatment in normal temperature and humidity.
The charge and discharge current of the capacitor must not exceed 50mA for IR measurement.
*Apply 1.0 times when the rated voltage is 4V or less. Applied voltages for respective products are indicated
in the chart below.
Capacitance Variation ≤ ±12.5%
Dissipation Factor / Tanδ ≤ Initial Value x 2.0 (See Above)
Insulation Resistance
Over 1000MΩ or 50MΩ・µF, whichever is less. *Exceptions
Listed Below
Load Humidity
Appearance No visual defects
Take the initial value after heat treatment.
After applying rated voltage for 500+12/ −0 hours in the condition of 40℃±2℃ and 90 to 95%RH, and place in normal
temperature and humidity, then measure the sample after heat treatment.
The charge and discharge current of the capacitor must not exceed 50mA for IR measurement.
Capacitance Variation ≤ ±12.5%
Dissipation Factor / Tanδ Within specication
Insulation Resistance
Over 1000MΩ or 50MΩ・µF, whichever is less.
*Exceptions Listed Below
Appearance No problem observed Microscope
Termination Strength No problem observed Apply a sideward force of 500g (5N) to a PCB-mounted sample. Note : 2N for 0201 size, and 1N for 01005 size.
Vibration
Appearance No problem observed
Take the initial value after heat treatment.
Vibration frequency: 10 to 55 (Hz)
Amplitude: 1.5mm
Sweeping condition: 10→55→10Hz/ 1 minute in X, Y and Z directions: 2 hours each, 6 hours in total, and place in normal
temperature and humidity, then measure the sample after heat treatment
Capacitance Within tolerance
Tanδ Within tolerance
Heat treatment Expose sample in the temperature of 150+0/ −10℃ for 1 hour and leave the sample in normal temperature and humidity for 24±2 hours.
Voltage to be applied in the High Temperature Load (Applied voltage is the multiple of the rated voltage)
Rated Voltage Products
×1.0
2.5V KGM03DS60E475
4V KGM03CS60G105, KGM05DS60G226, KGM15CS60G226, KGM21AS60G476
6.3V KGM03CS60J105, KGM05BS60J475, KGM05CS60J106, KGM15CS60J226
10V KGM03CS61A105, KGM05AS61A474, KGM05AS61A105, KGM05CS61A475, KGM15CS61A226, KGM21AS61A226
16V KGM05AS61C474, KGM05AS61C225, KGM15CS61C106, KGM21AS61C226
25V KGM05AS61E105
Load Life / Load Humidity > Insulation Resistance: Over 10MΩ · μF
S6
03 KGM03DS60E475, KGM03CS60G105, KGM03CS60J105, KGM03CS61A105
05
KGM05DS60G226, KGM05CS60J475, KGM05BS60J475, KGM05CS60J106, KGM05AS61A474, KGM05AS61A105, KGM05CS61A475, KGM05AS61C474, KGM05AS61C225,
KGM05AS61E105
15 KGM15CS60G226M, KGM15CS60J226, KGM15CS61A106, KGM15CS61A226, KGM15CS61C106
21 KGM21AS60G476, KGM21AS60J226, KGM21AS61A226, KGM21AS61C226
–
surface mount ceramic capacitor products
–
The Important Information/Disclaimer is incorporated in the catalog where these specications came from or available
online at www.kyocera-avx.com/disclaimer/ by reference and should be reviewed in full before placing any order.