Features and Application Notes
ISA
®
13 is known for low resistivity and a relatively low temperature
coefficient, as well as its relatively high corrosion resistance. It is
used for low-value resistors and for heating wires and mats in heating
cords and in heating cables. The maximum working temperature
in air is +200 °C. ISA
��
13 can also be used as welding wire, e. g.
for building-up welding in copper-plated steel-tanks, as well as for
tube-weldings.
Form of Delivery
ISA
®
13 is supplied in the form of round wires in the range 0.05 to
8.00 mm Ø in bare or enamelled condition, flat wires, stranded wires
and ribbons.
1) ISA
®
13 is a registered registered trademark of Isabellenhütte Heusler GmbH & Co. KG.
2) This value applies to wires of 2.0 mm diameter. For thinner wires the minimum values will substantially increase, depending on the dimensions.
Notes on Treatment // ISA
®
13 can be worked easily. This alloy
can be soldered and brazed without difficulty. All known welding
methods can be used.
Brand
Name
ISA
®
13
1)
Material
Code
2.1356
Abbreviation
CuMn3
Chemical Composition (mass components) in %.
Average values of alloy components
Cu
Rem.
Mn
3
Physical Characteristics (Reference Values)
Density at +20 °C
Melting point
Specific heat
at +20 °C
Wärmeleitfähig-
keit bei +20 °C
Average linear thermal expansion coefficient
between +20 °C and
Thermal EMF
against copper at
+100 °C +400 °C +20 °C
g/cm³ lb/cub in °C J/g K W/m K 10
-6
/K 10
-6
/K µV/K
8.80 0.32 +1,050 0.39 84.00 15.50 18.00 +1.00
Strength Properties at +20 °C in Annealed Condition
Tensile Strength
2)
Elongation (L
0
= 100 mm) % at nominal diameter in mm
MPa psi
0.020 to 0.063 > 0.063 to 0.125 > 0.125 to 0.50 > 0.50 to 1.00 > 1.00
290 42,050 ≈ 8 ≈ 15 ≈ 20 ≥ 20 ≥ 25
Electrical Resistance in Annealed Condition
Temperature coefficient
of electrical
resistance between
Electrical resistivity in: µΩ x cm (first line) and Ω/CMF (second line)
Reference Values
+20 °C and +105 °C
10
-6
/K
+20 °C
tolerance ±10 %
+100 °C +200 °C +300 °C +400 °C +500 °C
+280 to +380 12.5 12.9 13.3
75 75 80
1/3 Data sheets // ISA
®
13 // 7
Issue 29-March-2014